Harris® 15620R1 Brazing Alloy, 1/8 in Dia x 20 in L, Tube Container

Manufacturer: Harris Products Group
Harris®, 15620R1, Brazing Alloy, 1/8 in Diameter, 20 in Length, Tube Container, Chemical Composition: 4.8 to 5.2 % Phosphorus, 14.5 to 15.5 % Silver, 0.15 % Other, Copper Remainder, 704 to 816 deg C Brazing, Applicable Materials: Low Nickel/Copper/Nickel Base Metals
SKU: JWH 15620R1
Manufacturer part number: 15620R1
Availability:
Total Stock Available : 0
Price: Call for pricing
i h h

 

Have Questions About This Product?

 

STAY-SILV® 15 phos-copper filler metal is the industry standard for air conditioning/refrigeration applications. Its melting range is useful in filling wider clearances while providing good service ductility. Conforms to the EU Reach & RoHS directive.
  • Popular choice for copper brazing of air conditioning and refrigeration connections
  • Flows into tight connections when heated above its liquidus temperature
  • Excellent for situations where close fit-up does not exist and where thermal expansion and service vibration are involved
  • Wide melting range allows the operator to fill loose connections
  • Recommended joint clearance of 0.003 in - 0.006 in (0.08mm - 0.15mm)
  • Use STAY-SILV white flux to braze brass or copper-to-brass
  • Corrosion resistance is generally similar to the copper base metal, but phosphorus containing alloys, including STAY-SILV 15, should not be used if the braze is exposed to sulfur or sulfur compounds in service
  • Not recommended for brazing steel or other ferrous metals due to sufficient lack of joint ductility
  • Suitable for brazing low nickel (10% maximum) copper/nickel base metals